| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 吸水率 | 24hr，in 23℃ | ASTM D-570 | 0.2 | % | |
| 物理性能 | 比重 | --- | JIS K-7112 | 1.2 | --- | |
| 透光率 | 3mm thick | ASTM D-1003 | 88 | --- | ||
| 折射率 | --- | ASTM D-542 | 1585 | --- | ||
| 阻燃性 | 0.38mm | UL 94 | V-2 | --- | ||
| 机械性能 | 拉伸强度 | 屈服点 | --- | ASTM D-638 | 61(620) | Mpa(kgf/cm2) |
| 断裂点 | ASTM D-638 | 81(830) | Mpa(kgf/cm2) | |||
| 拉伸模量 | --- | ASTM D-638 | 2120(21600) | Mpa(kgf/cm2) | ||
| 拉伸率 | 屈服点 | --- | ASTM D-638 | 6 | % | |
| 断裂点 | ASTM D-638 | 140 | % | |||
| 弯曲强度 | --- | ASTM D-790 | 90(915) | Mpa(kgf/cm2) | ||
| 弯曲模量 | --- | ASTM D-790 | 2230(22700) | Mpa(kgf/cm2) | ||
| 压缩强度 | --- | ASTM D-695 | 76(770) | Mpa(kgf/cm2) | ||
| 耐冲击强度值 | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 880(90) | J/m(kgf?cm/cm) | ||
| 耐冲击强度值 | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 140(14) | J/m(kgf?cm/cm) | ||
| 洛氏硬度 | --- | ASTM D-785 | 77 | M标度 | ||
| 电气性能 | 耐导电径迹性（CTI） | --- | IEC 112 | 300 | V | |
| 绝缘破坏强度 | 快速加压值厚度1.6mm | ASTM D-149 | 30 | kv/mm | ||
| 体积电阻率 | --- | ASTM D-257 | 3×1016 | Ω.cm | ||
| 介电率 | 60Hz | ASTM D-150 | 2.95 | --- | ||
| 介电率 | 106Hz | ASTM D-150 | 2.9 | --- | ||
| 介电正切 | 60Hz | ASTM D-150 | 0.0004 | --- | ||
| 介电正切 | 106Hz | ASTM D-150 | 0.009 | --- | ||
| 耐电弧性 | --- | ASTM D-495 | 110 | sec | ||
| 加工性能 | 成型收缩率 | 流动方向 | --- | ASTM D-955 | 0.5～0.7 | % |
| 垂直方向 | ASTM D-955 | 0.5～0.7 | % | |||
| 热 性 能 | 负荷挠曲温度 | 负荷1.813MPa(18.6kgf/cm2) | JIS K-7207 | 133 | ℃ | |
| 负荷挠曲温度 | 负荷0.451MPa(4.6kgf/cm2) | JIS K-7207 | 143 | ℃ | ||
| 线膨胀系数 | 流动方向 | --- | ASTM D-696 | 7 | 10-5cm/cm/℃ | |
| 垂直方向 | ASTM D-696 | 7 | 10-5cm/cm/℃ | |||
| 温度指数 | 电学式 | 厚度1.47mm | UL 746B | 125 | ℃ | |
以上PC LV-2250Y塑料物性表仅供参考，请以实际操作为准！